Oil Filled Nylon 6
Oil filled nylon offers the following benefits over standard nylon:
• Reduced coefficient of friction (up to 50%).
• Increased wear resistance (up to x10).
Temperature: -40°C to +100°C, +160°C short term.
Applications: Ideal for unlubricated, highly loaded and slow moving parts.
Availability:
| Colour: |
Green. |
| Sheet Size (mm): |
2000 x 1000. |
| Thickness (mm): |
10 to 50. |
| Rod dia (mm): |
4 to 500. |
| Length (mm): |
3000. |
Technical Specification:
Information to be used as a guide only. It corresponds with our current knowledge and indicates possible applications. We cannot guarantee suitability for a specific application. Unless otherwise stated these values represent averages taken from injection moulded samples.
| Product |
Test Method |
Notes |
Metric Units |
Imperial Units |
| Density |
ISO 1183:1987 |
Test Method A |
g/cm3 |
1.140 |
lb/inch3 |
0.041 |
| Moisture Absorption (Saturation) |
ISO 62:1999 |
Immersion 23ºC |
% |
4 |
% |
4 |
| Mechanical |
| Tensile Strength |
ISO 527-1/2:1993 |
Sample 1B, 50mm min -1 |
MPa |
75 |
psi |
10878 |
| E-Modulus |
ISO 527-1/2:1993 |
Sample 1B, 50mm min -1 |
MPa |
3800 |
psi |
551145 |
| Elongation at Break |
ISO 527-1/2:1993 |
Sample 1B, 50mm min -1 |
% |
>25 |
% |
>25 |
| Compressive Strength |
ISO 604:2002 |
Sample Type B, 5mm min -1 |
MPa |
95 |
psi |
13779 |
| Compressive Modulus |
ISO 604:2002 |
Sample Type A 1mm min -1 |
MPa |
2400 |
psi |
348091 |
| Flexural Strength |
ISO 178:2001 |
1.5mm min -1 |
MPa |
95 |
psi |
13779 |
| Flexural Modulus |
ISO 178:2001 |
1.5mm min -1 |
MPa |
3000 |
psi |
435114 |
| Izod Impact Strength |
ISO 180:2000 |
Sample Type A (notched) |
KJ/m2 |
5.80 |
ft.lb/in2 |
2.76 |
| Hardness Shore D |
ISO 868:2003 |
|
|
83 |
|
83 |
| Coefficient of Friction (Dynamic) |
|
31.4m/min, 1.75MPa |
|
0.19 |
|
0.19 |
| Wear Rate |
|
31.4m/min, 1.75MPa |
mg/km |
0.15 |
|
|
| K-Factor |
|
31.4m/min, 1.75MPa |
mm3/Nm |
1.70 x 10-6 |
in3.min./ft.lb.hr |
0.84 x 10-9 |
| Thermal |
| Melting Temperature |
|
|
ºC |
220 |
ºF |
428 |
| Maximum Intermittent Service Temperature |
|
|
ºC |
170 |
ºF |
338 |
| Maximum Continuous Service Temperature |
|
|
ºC |
110 |
ºF |
230 |
| Minimum Intermittent Service Temperature |
|
|
ºC |
-100 |
ºF |
-148 |
| Minimum Continuous Service Temperature |
|
|
ºC |
-40 |
ºF |
-40 |
| Coefficient of Linear Thermal Expansion (TMA) |
ISO 11359-2:1999 |
23ºC - 55ºC |
ºC-1 |
8 x 10-5 |
ºF-1 |
4.44 x 10-1 |
| Flammability |
IEC 60695-11-10:2003 |
|
|
HB |
|
HB |
| Electrical |
| Dielectric Constant |
IEC 60250:1969-01 |
1MHz |
|
3.7 |
|
3.7 |
| Dielectric Strength |
IEC 60243-1:1998-01 |
|
kV/mm |
25 |
kV/In |
635 |
| Volume Resistivity |
IEC 60093: 1980-01 |
|
ohm.m |
1 x 1013 |
ohm.in |
3.93 x 1014 |
| Surface Resistivity ROA |
IEC 60093: 1980-01 |
|
ohm |
1 x 1012 |
ohm |
1 x 1012 |
| Comparitive Tracking Index |
IEC 60112:2003-01 |
|
CTI |
600 |
CTI |
600 |
The information shown above corresponds with our current knowledge of our products. We accept no responsibility in respect of application, conversion or use made of our products.