PPS Glass Filled 40
PPS glass Filled is a 40 % glass fibre reinforced semi-crystalline high performance plastic with very high rigidity and strength for demanding applications.
Key Features:
High thermal mechanical strength
Good chemical and hydrolysis resistance, even against steam
Good machinability
High creep strength
Very rigid
Good dimensional accuracy
Electrically insulating
Excellent wer resistance
Self-extinguishing V-0
Applications:
Plug parts, high strength thermal mechanical components, pump housing parts, thrust / distance pieces, light sockets, catalyst supports, flanges, friction pads, valve bodies.
Technical Information
Information to be used as a guide only. It corresponds with our current knowledge and indicates possible applications. We cannot guarantee suitability for a specific application. Unless otherwise stated these values represent averages taken from injection moulded samples.
| Properties |
Unit |
Test Method DIN ASTM |
Result |
| Mechanical |
- |
- |
- |
| Density |
g/cm³ |
53479 |
1.64 |
| Tensile strength at yield |
MPa |
53455 |
- |
| Tensile strength at break |
MPa |
53455 |
160 |
| Elongation at Break |
% |
53455 |
1.6 |
| Modulus of elasticity in tension |
MPa |
53457 |
14000 |
| Modulus of elasticity in flexure |
MPa |
53457 |
13000 |
| Ball indentation hardness |
MPa |
53456 |
>300 |
| Impact strength (Charpy) |
KJ/m² |
53453 |
35 |
| Creep rupture strength after 1000 hours with static load |
MPa |
- |
- |
| Time yield limit for 1% elongation after 1000 hours |
MPa |
- |
- |
| Coefficient of friction against hardened and ground steel p+0,05 N/mm2, v=0,6 m/s |
- |
- |
- |
| Wear conditions as above |
µm/km |
- |
- |
| Thermal |
- |
- |
- |
| Crystalline melting point |
ºC |
53736 |
285 |
| Glass transition temperature |
ºC |
53736 |
88 |
| Heat distortion temperature method A |
ºC |
ISO 75 |
260 |
| Heat distortion temperature method B |
ºC |
ISO 75 |
- |
| Max. service temperature short term |
ºC |
- |
260 |
| Max. service temperature long term |
ºC |
- |
230 |
| Coefficient of thermal conductivity |
W/(m K) |
- |
0.2 |
| Specific heat |
J/(g K) |
- |
- |
| Coefficient of thermal expansion |
10-5/K |
- |
~3 |
| Electrical |
- |
- |
- |
| Dielectric constant at 10 (5) Hz |
- |
53483 |
4 |
| Dielectric loss factor at 10(5) Hz |
- |
53483 |
0.004 |
| Specific Volume Resistance |
Ωcm |
53482 |
10 (15) |
| Surface Resistance |
O |
53482 |
- |
| Dielectric strength 1mm |
kV/mm |
53481 |
20 |
| Tracking resistance |
- |
53480 |
KC175 |
| Miscellaneous |
- |
- |
- |
| Moisture Absorption: Equilibrium in standard atmosphere (23ºC / 50% relative humidity) |
% |
53714 |
- |
| Water absorption at saturation at 23ºC |
% |
53495 |
1 |
| Resistance to hot water, washing soda |
- |
- |
resistant |
| Flamability |
- |
UL 94 |
VO |
| Resistance to weathering |
- |
- |
not resistant |