KLINGER Graphite PSM-AS
Pure exfoliated graphite with a tanged stainless steel 316 reinforcement for improved blow out resistance.
Due to the excellent chemical and thermal capabilities of graphite it is used extensively throughout the petrochemical and chemical industries for process duties and steam applications.
Key Features:
- Excellent resistance to steam
- Resistant to virtually all media
- Outstanding resistance to high and low temperature
- High compressibility
- Good leakage properties
- Unlimited storage life
- Anti-stick finish on both sides
Availability:
| Sheet size (mtrs): |
1.0 x 1.0*, 1.5 x 1.5 |
| Thickness (mm): |
0.8, 1.0, 1.5, 2.0, 3.0 |
*Donates standard size
Application Guidelines:
1. Usually satisfactory without reference.
2. Usually satisfactory but suggest you refer to PAR for advice.
3. Caution, definitely refer to PAR and consider another grade of material
*Chemical compatibility must be considered in all cases*
Tests and Certifications:
- BAM Approval for use with oxygen 130 bar/200ºC
- WRc Approval
- DIN DVGW NG-5124AT0417
- Firesafe according to BS 5146
Technical Information:
| Compressibility ASTM F36A |
* |
33-38% |
| Recovery ASTM F 36 A |
* |
13-18% |
| Stress relaxation DIN 52913 |
50MPa, 16h/300ºC |
min 48MPa |
| Klinger cold/hot compression (50MPa) |
Thickness decrease 23ºC
Thickness decrease at 300ºC |
40%
1.5% |
| Gas leakage DIN 3535/6 |
* |
0.8ml/min |
| Chlorides (soluble) |
* |
<40ppm |
| Fluoride and chloride content |
* |
<200ppm |
| Density |
* |
1.0g/cm³ |
| Max Temperature |
* |
460ºC |
| Max Pressure |
* |
150 bar |
| Purity |
* |
min 98% |
We also offer an unbranded graphite gasket material. Click here for material datasheet