KLINGERsil C8200
Unique blend of fibres with an acid resistant binder. Specifically developed for aggressive chemical environments.
Key Features:
- Resistant to most mineral acids
- Resistant to alkalis, ketones, aldehydes
- Resistant to many refrigerants
- Resistant to oils, fuels, hydrocarbons etc.
- 3xA anti-stick finish on both sides
Applications:
Specifically developed for aggressive chemical environments. Resists most mineral acids, alkalis, ketones, aldehydes, refrigerants, oils fuels and hydro carbons.
Availability:
| Sheet size (mtrs): |
2.0 x 1.5*, 1.5 x 1.0 |
| Thickness (mm): |
0.5, 0.75, 1.0, 1.5, 2.0, 3.0 |
*Donates standard sheet size
Application Guidelines:
1. Usually satisfactory without reference.
2. Usually satisfactory but suggest you refer to PAR for advice.
3. Caution, definitely refer to PAR and consider another grade of material
*Chemical compatibility must be considered in all cases*
Technical Information:
| Compressibility ASTM F36A |
* |
9% |
| Recovery ASTM F 36 A |
* |
55% |
| Klinger cold/hot compression (50MPa) |
Thickness decrease 23ºC
Thickness decrease at 300ºC |
7%
17% |
| Gas leakage DIN 3535/6 |
* |
<1.0ml/min |
| Chlorides (soluble) |
* |
150ppm |
| Thickness increase after fluid immersion ASTM F 146 |
H²SOª, 96% : 18h/23ºC
HNO³, 96% : 18h/23ºC
H²SOª, 65% : 48h/23ºC |
10%
Unsuitable
8% |
| Density |
* |
1.7 g/cm³ |
| Max Temperature |
* |
200ºC |
| Max Pressure |
* |
60 bar |
| Average Surface Resistance |
ROA (xE4) |
8.3 Ω |
| Average Specific Volume Resistance |
?D (xE4) |
1.2 O cm |
| Average Power Factor |
* |
17.5 kV/mm |
| Average dielectric strength |
1kHz,ca. 3mm thick |
0.27 tan d |
| Average dielectric constant |
1kHz,ca. 3mm thick |
8.4er |